Título:	Efeitos de diferentes materiais à base de silicato de cálcio na resistência à fratura de dentes permanentes imaturos com reabsorção radicular por substituição e na osteoclatogênese: um estudo laboratorial
Autor(es):	Freitas, Gabrielle Alves Nunes
Primeiro orientador:	Moura, Camilla Christian Gomes
Primeiro coorientador:	Souza, Gabriela Leite de
Primeiro membro da banca:	Soares, Priscilla Barbosa Ferreira
Segundo membro da banca:	Soares, Carlos José
Terceiro membro da banca:	Peres, Thiago Silva
Resumo:	Objective(s): This study evaluated the effects of Biodentine (BD), Bio-C repair (BCR), and mineral trioxide aggregate plug (MTA) on fracture resistance of simulated immature teeth with replacement root resorption (RRR) and in vitro induced osteoclastogenesis. Materials and Methods: Sixty bovine incisors simulating immature teeth and RRR were divided into five groups: BD and BCR, completely filled with respective materials; MTA, a 3-mm apical plug of MTA; RRR, no root canal filling (negative control); PL, no RRR, and root canal filling performed (positive control). All the teeth underwent mechanical fatigue, and then compression strength testing was performed using an Instron universal testing machine. RAW 264.7 macrophages were treated with 1:16 extracts of BD, BCR, and MTA containing receptor activator of nuclear factor-kappa B ligand (RANKL) for 5 days. RANKL-induced osteoclast differentiation was assessed by staining with tartrate-resistant acid phosphatase. Fracture load and osteoclast number were analyzed using one-way analysis of variance (ANOVA) and Tukey’s test (α=0.05). Results: No significant difference in fracture resistance was observed among the groups (P>0.05). All materials similarly inhibited osteoclastogenesis (P>0.05), except for BCR, which showed a lower percentage of osteoclasts than MTA (P<0.0001). The presence of RRR did not affect the fracture strength of the simulated immature teeth and the materials tested did not significantly strengthen them. Conclusion(s): The treatment options used to treat non-vital immature teeth with RRR do not strengthen them and provide similar resistance to fractures. BD, MTA, and BCR showed inhibitory effects on osteoclast differentiation, with BCR group showing better results.
Palavras-chave:	Fracture strength Non-vital tooth Osteoclastogenesis Root resorption Silicate cement
Área(s) do CNPq:	CNPQ::CIENCIAS DA SAUDE
Idioma:	eng
País:	Brasil
Editora:	Universidade Federal de Uberlândia
Referência:	FREITAS, Gabrielle Alves Nunes. Efeitos de diferentes materiais à base de silicato de cálcio na resistência à fratura de dentes permanentes imaturos com reabsorção radicular por substituição e na osteoclatogênese: um estudo laboratorial. 2022. 26 f. Trabalho de Conclusão de Curso (Graduação em Odontologia) – Universidade Federal de Uberlândia, Uberlândia, 2023.
URI:	https://repositorio.ufu.br/handle/123456789/36700
Data de defesa:	5-Dez-2022
Aparece nas coleções:	TCC - Odontologia

Este item está licenciada sob uma Licença Creative Commons