Título: Estudo da aplicabilidade de ferramentas refrigeradas internamente na usinagem de ferro fundido cinzento
Título(s) alternativo(s): Study of the applicability of internally cooled tools on gray cast iron machining
Autor(es): Bazon, Victor Tallis
Primeiro orientador: Silva, Marcio Bacci da
Primeiro coorientador: Fernandes, Gustavo Henrique Nazareno
Primeiro membro da banca: Ziberov, Maksym
Resumo: Neste trabalho foi proposta uma nova técnica inovadora que utiliza o conceito de refrigeração interna à ferramenta de corte. Para isso realizou-se um estudo sobre o comportamento de ferramentas de metal duro, refrigeradas internamente, no torneamento de Ferro Fundido Cinzento por Fundição Contínua (FoFo). As variáveis de entrada do processo foram: velocidade de corte (𝑉𝑐) (100 e 150 m/min), profundidade de corte (𝑎𝑝) (1,0 e 2,0 mm) e ambientes, Fluido de Corte Abundante (FCA) e Ferramenta Refrigerada Internamente (FRI). As variáveis resposta foram: força de usinagem e integridade superficial (rugosidade, microdureza e metalografia) além de tipos e mecanismos de desgaste. Os principais resultados indicaram que as força de corte foram maiores com a utilização das FRIs, em comparação com o FCA, sendo um possível indicativo do efeito da maior capacidade de refrigeração das FRIs. Em relação à rugosidade, para maior velocidade de corte (150 m/min), portanto maior geração de calor e temperatura, o ambiente FRI apresentou melhores resultados. A análise de microdureza subsuperficial indicou que ambos os processos, FRI e FCA, como esperado, causaram encruamento do material. O método FRI apresentou resultados maiores de microdureza, possivelmente por conta da baixa capacidade lurificante do sistema. O tipo de desgaste mais evidente nas ferramentas de corte foi o desgaste de flanco, enquanto os mecanismos predominates foram de adesão (atrittion), comuns em baixas velocidades de corte assim como o desgaste abrasivo.
Abstract: In this work, an innovative technique was proposed using the concept of internal cooling of the cutting tool. For this purpose, a study was carried out on the behavior of carbide tools, internally cooled, in the turning of Gray Cast Iron by Continuous Casting (FoFo). The process input variables were: cutting speed (𝑉𝑐) (100 and 150 m / min), cutting depth (𝑎𝑝) (1.0 and 2.0 mm) and environments, Abundant Cutting Fluid (ACF) and Internally Cooled Tool (ICT). The response variables were: cutting forces, surperficial integrity (roughness, microhardness and metallography) as well as types and mechanisms of wear. The main results indicated that the cutting forces were greater with the use of ICT, in comparison with the ACF, being a possible indication of the effect of the greater cooling capacity of ICTs. In relation to roughness, for a higher cutting speed (150 m/min), therefore greater heat and temperature generation, the ICT environment showed better results. The analysis of subsurface microhardness indicated that both processes, ICT and ACF, as expected, caused hardening of the material. The ICT method showed higher results of microhardness, possibly due to the low lurifying capacity of the system. The most evident type of wear on cutting tools was flank wear, while the predominant mechanisms were adhesion (atrittion), common at low cutting speeds as well as abrasive wear.
Palavras-chave: Ferro fundido cinzento
Torneamento
Ferramenta refrigerada internamente
Fluido de corte abundante
Área(s) do CNPq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA::PROCESSOS DE FABRICACAO
Idioma: por
País: Brasil
Editora: Universidade Federal de Uberlândia
Referência: BAZON, Victor Tallis. Estudo da aplicabilidade de ferramentas refrigeradas internamente na usinagem de ferro fundido cinzento. 2020. 73 f. Trabalho de Conclusão de Curso (Graduação em Engenharia Mecânica) – Universidade Federal de Uberlândia, Uberlândia, 2020.
URI: https://repositorio.ufu.br/handle/123456789/31150
Data de defesa: 21-Dez-2020
Aparece nas coleções:TCC - Engenharia Mecânica

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
EstudoDaAplicabilidade.pdf12.51 MBAdobe PDFThumbnail
Visualizar/Abrir


Este item está licenciada sob uma Licença Creative Commons Creative Commons