| Document type: | Trabalho de Conclusão de Curso |
| Access type: | Acesso Aberto |
| Title: | Avaliação do comportamento tribológico de revestimentos de Inconel 625 no desgaste por deslizamento |
| Alternate title (s): | Evaluation of the tribological behavior of 625 inconel coatings in slip wear |
| Author: | Ramos, Matheus Santana |
| First Advisor: | Silva Junior, Washington Martins da |
| First member of the Committee: | Santos, Regina Paula Garcia |
| Second member of the Committee: | Teles, Vinícius Carvalho |
| Summary: | O presente trabalho objetivou avaliar a resistência ao desgaste por deslizamento do aço A36 revestido com Inconel 625, comparando com outros dois revestimentos, um de aço inoxidável 316 e outro de Inconel 625 sobreposto ao aço inoxidável 316. As amostras foram lixadas e polidas. Para realizar os ensaios, foi utilizado o Tribômetro Universal Plint® (modelo TE 67 Plint and Partners LDT) na configuração movimento alternado. A carga de teste utilizada foi de 21,5 N e o contra corpo adotado foram esferas de 10 mm. Foram feitos três ensaios para cada amostra. Após a realização dos testes, foi verificado que, apesar de possuir um coeficiente de atrito maior que a amostra com revestimento de aço inox, a amostra de revestimento com Inconel 625 apresenta menor desgaste. |
| Abstract: | The purpose of this study was to evaluate the sliding wear resistance of the A36 steel coated with Inconel 625 in comparison to another two coatings: 1- 316 stainless steel and 2- Inconel 625 superimposed on 316 stainless steel. The samples were sanded and polished. Tests were performed in the Universal Plint® Tribometer (model TE 67 Plint and Partners LDT) using the reciprocating configuration. The test load was set to 21.5 N and the counter body was 10 mm steel beads. Three tests were performed in each sample. Despite having a coefficient of friction higher than the sample with stainless steel coating, the Inconel 625 coating sample presented a lower wear rate. |
| Keywords: | Inconel 625 Desgaste Deslizamento Revestimento Resistência Aço Atrito Tribômetro Movimento Alternado |
| Area (s) of CNPq: | CNPQ::ENGENHARIAS::ENGENHARIA MECANICA |
| Language: | por |
| Country: | Brasil |
| Publisher: | Universidade Federal de Uberlândia |
| Quote: | RAMOS, Matheus Santana. Avaliação do comportamento tribológico de revestimentos de Inconel 625 no desgaste por deslizamento. 2018. 50 f. Trabalho de Conclusão de Curso (Graduação em Engenharia Mecânica) – Universidade Federal de Uberlândia, Uberlândia, 2019. |
| URI: | https://repositorio.ufu.br/handle/123456789/25915 |
| Date of defense: | 10-Dec-2018 |
| Appears in Collections: | TCC - Engenharia Mecânica |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| AvaliaçãoComportamentoTribológico.pdf | TCC | 1.85 MB | Adobe PDF |  View/Open |
This item is licensed under a Creative Commons License