Tipo de acceso: Acesso Aberto
Título: Análise mecânica e microestrutural das ligas de níquel-cromo e cobalto-cromo de uso odontológico após refundição
Autor: Martins, Raquel Ribeiro
Primer orientador: Castro, Morgana Guilherme de
Primer coorientador: Simamoto Júnior, Paulo César
Primer miembro de la banca: Castro, Morgana Guilherme de
Segundo miembro de la banca: Turrioni, Ana Paula Silveira
Tercer miembro de la banca: Araújo, Paula Caetano
Resumen: Ligas de Níquel-Cromo (Ni-Cr) e Cobalto-Cromo (Co-Cr) são utilizadas para confecção de infraestruturas metálicas para próteses fixas e removíveis. Em virtude de fatores econômicos, alguns laboratórios reaproveitam essas ligas odontológicas. Tal fato, pode levar à perda qualitativa e quantitativa dos elementos das ligas e acarretar diferenças em suas propriedades, sendo um grande indicativo de falhas. Avaliou-se por meio de ensaio mecânico de resistência à flexão, microscopia eletrônica de varredura (MEV) e espectrômetro de energia dispersiva (EDS), o comportamento mecânico, das ligas de Ni-Cr e Co-Cr após fundição e refundição. Confecciou-se 40 barras (40 x 4 mm) divididas em 4 grupos (n =10): G1 (Ni-CrP) e G2 (CoCrP) composto por ligas puras; G3 (Ni-CrR), composto por 50% de liga de Ni-Cr puro e 50% da liga refundida e G4 (CoCrR) por 50% Co-Cr puro e 50% da liga refundida. Após fundição, submeteu-se as amostras à inspeção radiográfica e teste de resistência à flexão de três pontos. Após a fratura, levou-se as amostras em MEV para caraterização do padrão de fratura e em EDS para análise química semi-quantitativa. Não houve diferença estatisticamente significante entre os tipos de ligas (P=.324) e entre tipos de ligas e tipos de tratamentos (P=.841). Entretanto, houve diferença estatisticamente significante entre os tipos de tratamento (P=.01). A análise por EDS não mostrou alterações significativas quanto à composição química. Conclui-se que o processo de refundição em ligas de Co-Cr e Ni-Cr influência nos valores de resistência do material; portanto recomenda-se uma única utilização das ligas para trabalhos protéticos.
Abstract: Nickel-Chromium (Ni-Cr) and Cobalt-Chromium (Co-Cr) alloys are used for the fabrication of metal infrastructures for fixed and removable prostheses. Due to economic factors, some laboratories reuse these dental alloys. This fact can lead to the qualitative and quantitative loss of the elements of the alloys and to cause differences in their properties, being a great indicator of failures. The mechanical behavior of Ni-Cr alloys and Co-Cr alloys after melting and melting were evaluated by means of mechanical test of flexural strength, scanning electron microscopy (SEM) and dispersive energy spectrometer (EDS). 40 bars (40 x 4 mm) were divided into 4 groups (n = 10): G1 (Ni-CrP) and G2 (CoCrP) composed of pure alloys; G3 (Ni-CrR), composed of 50% pure Ni-Cr alloy and 50% recast alloy and G4 (CoCrR) by 50% pure Co-Cr and 50% recast alloy. After casting, the samples were subjected to radiographic inspection and three-point flexural strength test. After the fracture, samples were taken in SEM to characterize the fracture pattern and in EDS for semi-quantitative chemical analysis. There was no statistically significant difference between the types of alloys (P = .324) and between types of alloys and types of treatments (P =.841). However, there was a statistically significant difference between the types of treatment (P =.01). The ESD analysis showed no significant changes in chemical composition. It was concluded that the process of melting of Co-Cr and Ni-Cr alloys influence the strength values of the material; therefore a single use of alloys for prosthetic work is recommended.
Palabras clave: Fundição
Ligas dentárias
Materiais Dentários
Dental Casting Investment
Dental Alloys
Dental materials
Área (s) del CNPq: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
Idioma: por
País: Brasil
Editora: Universidade Federal de Uberlândia
Cita: MARTINS, Raquel Ribeiro.Análise mecânica e microestrutural das ligas de níquel-cromo e cobalto-cromo de uso odontológico após refundição. 2017. 35 f. Trabalho de Conclusão de Curso (Graduação em Odontologia) Universidade Federal de Uberlândia, Uberlândia, 2017.
URI: https://repositorio.ufu.br/handle/123456789/19976
Fecha de defensa: 10-nov-2017
Aparece en las colecciones:TCC - Odontologia

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
AnáliseMecânicaMicroestrutural.pdf3.21 MBAdobe PDFVista previa
Visualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.