Title: Propriedades ópticas do poliestireno sulfonado dopado com íons de neodímio
metadata.dc.creator: Silva, Marcelo Castanheira da
metadata.dc.contributor.advisor1: Marletta, Alexandre
metadata.dc.contributor.referee1: Cury, Luiz Alberto
metadata.dc.contributor.referee2: Barbosa Neto, Newton Martins
metadata.dc.description.resumo: Nesse trabalho apresentamos a síntese e caracterização óptica de filmes de poliestireno sulfonado (PSS) dopados com íons de neodímio (Nd), utilizando uma rota sintética simples e de baixo custo. O dopante utilizado foi o nitrato de neodímio. A incorporação máxima de íons Nd3+ na matriz, obtida na síntese dos filmes, ficou em torno de 14,0 %. Os espectros de absorção no UV-Vis-NIR dos filmes de Nd-PSS apresentaram as bandas características para o neodímio em solução aquosa. Os espectros de FTIR apresentaram um alargamento significativo das bandas em relação ao espectro de poliestireno sulfonado. Nesse mesmo espectro ocorre uma grande mudança na forma de linha do filme Nd-PSS na região abaixo de 1400 cm-1 referente à vibração da ligação N-O. Os filmes medidos por espectroscopia Raman apresentaram a mesma intensidade e localização dos picos, independentemente da região de incidência do laser na amostra. A análise desses espectros demonstra a superposição das bandas de: estiramento da ligação S-O, estiramento assimétrico do nitrato e a dobra fora do plano da ligação N-O. Esse fato comprova a dopagem do H-PSS e que o filme Nd07 (contendo a solução precursora de neodímio 0,7 mol/L) é o mais concentrado. Os espectros de luminescência no UV-Vis mostraram que quando se dopa a matriz polimérica PSS ocorre um deslocamento para o azul. Os espectros de luminescência com excitações em 458 nm (banda de absorção do H-PSS) e em 514 nm (banda de absorção do íon Nd3+) indicam que há um favorecimento da emissão em torno de 520 nm (verde) e de 610 nm (alaranjado), respectivamente. Os espectros de excitação seletiva mostram que há uma superposição das bandas de excitação do PSS com o Nd-PSS, quando o comprimento de onda de excitação varia de 400 até 500 nm. Acima de 500 nm, as bandas do Nd-PSS se alargam e ficam mais definidas. Os filmes de Nd-PSS apresentam uma intensa emissão no infravermelho em 1076 nm (transição radiativa 4F3/2®4I11/2). Não foi observada nenhuma dependência com a concentração em todos os espectros realizados. O fator de qualidade espectroscópica do filme Nd11, obtido pelos parâmetros de Judd-Ofelt, indica que ocorre o domínio da transição 4F3/2 ® 4I11/2 em 1076 nm, corroborando com os resultados das medidas feitas via fotoluminescência e infravermelho. Isso confirma que o filme Nd11 é um ótimo candidato para ser usado em dispositivos ópticos.
Abstract: In this work we present the synthesis and optic characterization of sulfonated polystyrene films (PSS) doped with ions of neodymium (Nd). The synthesis has a low cost and a simple route. The used dopant was the neodymium nitrate. The maximum incorporation of ions Nd3+ in the matrix, gotten in the synthesis of the films, was around 14.0 %. The absorption spectra in UV-Vis-NIR of the films of Nd-PSS had presented the characteristic bands for neodymium in aqueous solution. The FTIR spectra had presented a significant widening of the bands in relation to the sulfonated polystyrene spectrum. In this same spectrum occurs a great change in the form of line of the Nd-PSS film in the region below of 1400 cm-1 referring to the vibration of linking N-O. The films measured by Raman spectroscopy have presented the same intensity and localization of the peaks, independently of the region of incidence of the laser in the film. The analysis of these spectra demonstrates the overlapping of the bands: stretching of linking S-O, anti-symmetrical stretching of nitrate and the fold is of the plan of linking N-O. This fact proves the doping of the H-PSS and that the Nd07 film (contends the precursory neodymium solution 0.7 mol/L) is of higher concentration. The luminescence spectrum in UV-Vis region had shown that when the PSS polymer matrix is doped a blue shift is observed. The luminescence spectra excited in 458 nm (absorption band of the HPSS) and in 514 nm (absorption band of the Nd3+ ion) indicate, respectively, that it has an aiding of the emission around 520 nm (green) and of 610 nm (orange). The spectra of selective excitement show that it has an overlapping of the bands of excitement of the PSS with the Nd-PSS, when the wavelength of excitement varies of 400 until 500 nm. The bands of the Nd-PSS became wider and are more definite. The films of Nd- PSS present an intense emission in the infrared in 1076 nm (radiative transition 4F3/2®4I11/2). It was not observed dependence with the concentration in all spectra done. The factor of spectroscopic quality of the Nd11 film, gotten for the parameters of Judd-Ofelt, indicates that the domain of the transistion occurs in 4F3/2 ® 4I11/2 (1076 nm), proving with the results of the measures made in the photoluminescence in the infra-red. This confirms that the Nd11 film is an excellent candidate to be used in optic devices.
Keywords: Poliestireno sulfonado
Íons de neodímio
Propriedades ópticas
Polystyrene sulfonated
Neodymium ions
Optical properties
Polímeros
metadata.dc.subject.cnpq: CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA
metadata.dc.language: por
metadata.dc.publisher.country: BR
Publisher: Universidade Federal de Uberlândia
metadata.dc.publisher.initials: UFU
metadata.dc.publisher.department: Ciências Exatas e da Terra
metadata.dc.publisher.program: Programa de Pós-graduação em Física
Citation: SILVA, Marcelo Castanheira da. Propriedades ópticas do poliestireno sulfonado dopado com íons de neodímio. 2006. 160 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de Uberlândia, Uberlândia, 2006.
URI: https://repositorio.ufu.br/handle/123456789/15649
Issue Date: 23-May-2006
Appears in Collections:DISSERTAÇÃO - Física

Files in This Item:
File Description SizeFormat 
MCSilvaDISSPRT.pdf2.11 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.