Esse estudo tem como objetivo avaliar o desempenho biomecânico por meio da
resistência máxima à tração (UTS, MPa), Força de Ruptura (RF, N) e elongação (%)
de 21 lençóis no mercado para isolamento absoluto. Vinte e um lençóis de borracha
foram testados: All Prime; Madeitex; Sanctuary Black, Green, Blue, Non látex;
Nictone Blue, Black; Mk life; Elastidam; Bassi; Pribanic; Care; OK; MDC dental;
Keystone; Dura Dam; Flexi dam; Sanctuary Blue; Nictone Blue; Ehros; USE. As
amostras (n=15) foram cortadas seguindo o padrão ISO 9001 (medidas de 80 × 10
mm, com um furo de 1,74 mm no centro). Foram testadas com uma máquina de
ensaios universal (EMIC) com célula de carga de 500 N e carga de tração a uma
velocidade de 500 mm/min até a ruptura. Foram realizadas análises de MEV, EDS,
espessura e radiopacidade. Dados foram analisados por ANOVA de um fator e teste
de Tukey (α = 0,05). Nictone teve a maior espessura (0,4 mm folha grossa e 0,3 mm
média) e o maior valor de RF (35,5 N). Os demais produtos apresentaram valores de
UTS variando entre 19N - 30 N. O lençol Bassi apresentou maiores valores de UTS.
Observou-se defeitos estruturais que podem comprometer a contaminação do
campo operatório em alguns produtos testados. Os elementos predominantes foram
C, Mg, S, Si e Ca. As propriedades mecânicas variaram substancialmente,
expressando a falta de padronização dos lençóis encontrados no mercado. A
maioria dos diques de borracha apresenta propriedades mecânicas e físicas
adequadas para o uso clínico. O maior custo de mercado não reflete em melhor
desempenho biomecânico dos lençóis de borracha.
Abstract
Objective: This study aims to evaluate the mechanical and physical properties of
dental dam sheets used for absolute isolation and to correlate the mechanical
parameters with cost.
Methods and materials: Twenty-one dental dam sheets were tested: All Prime;
Madeitex; Sanctuary non-latex, Sanctuary latex black, green, and blue; Nic Tone
blue and black; Mk Life; Elastidam; Bassi; Pribanic; Care; OK; MDC Dental;
Keystone; Dura Dam; Flexidam; Sanctuary blue; Nic Tone blue; Ehros; and USE.
The thicknesses of the dental dam sheets were measured using a digital micrometer
(Mitutoyo). Dental dam sheets (n = 15) were prepared by cutting the samples
following the ISO 9001 standard, with dimensions of 80 mm × 10 mm and a 1.7 mm
hole made at the center of each specimen. The specimens were tested using a
universal testing machine (Emic) at a speed of 500 mm/min until rupture to calculate
their thickness (mm), rupture force (RF, N), elongation (%), and ultimate tensile
strength (UTS, MPa) scanning electron microscopy and X-ray energy dispersive
spectroscopy analyses were performed. The radiopacity was measured using digital
radiography. Thickness, UTS, RF, and elongation data were analyzed by one-way
ANOVA and Tukey’s test (α = 0.05).
Results: Flexidam dental dam had the thickest (0.5 mm), while Nic Tone had a
medium thickness of 0.3 mm; the RF value (41.3 N) was also higher for thick dental
dams. The other samples had RF values ranging from 19 to 30 N. The highest
elongation was obtained for the non-latex Sanctuary dental dam (600 mm). The
Bassi dental dam had the highest UTS value (15 MPa), and medium and small
particles were observed in most of the gums. A loss of continuity was detected in the
structure of Sanctuary green and blue media. The predominant elements in the
sheets were carbon, magnesium, sulfur, silicon, and calcium.
Conclusions: The mechanical properties demonstrated by the UTS, RF, and
elongation varied substantially, indicating a lack of standardization of dental dam
sheets. Most of the dental dams studied have mechanical and physical properties
suitable for clinical use. The correlation coefficient between the cost and mechanical
properties was very low.
Palavras-chave
Lençol de borracha, Propriedades mecânicas, Custo, Testes mecãnicos
Citação
JUNQUEIRA, Paulo César Bandeira. Isolamento absoluto: aspectos biomecânicos e características físicas de lençóis de borracha. 2024. 29 f. Trabalho de Conclusão de Curso (Graduação em Odontologia) - Universidade Federal de Uberlândia, 2024.
DOI
Coleções
Avaliação
Revisão
Suplementado Por
Referenciado Por
Licença Creative Commons
Exceto quando indicado de outra forma, a licença deste item é descrita como Acesso Embargado