| Título: | Análise da integridade da superfície e do desvio dimensional de aço rolamento pela técnica da impedância eletromecânica após retificação cilíndrica de mergulho |
| Título(s) alternativo(s): | Analysis of the surface integrity and dimensional accuracy of bearing steel after cylindrical plunge grinding for Impedance-Based |
| Autor(es): | Resende, Paulo Vinicius da Silva |
| Primeiro orientador: | Silva, Rosemar Batista da |
| Primeiro membro da banca: | Ventura, Carlos Eiji Hirata |
| Segundo membro da banca: | Santos, Marcelo Braga dos |
| Resumo: | Dentre as peculiaridades dos processos de retificação com rebolos de abrasivos convencionais, o destaque é para a elevada energia específica na zona de corte o que faz com que a maior parte do calor gerado seja direcionado à peça, potencializando, portanto, a ocorrência de danos térmicos e distorções na mesma. Por essa razão, o monitoramento da integridade superficial é crucial para garantir a qualidade do produto acabado, sobretudo por meio de métodos não destrutivos. Dentre estes métodos, a técnica da impedância eletromecânica (IEM) tem mostrado resultados promissores e confiáveis para monitorar a integridade de peças retificadas. Neste sentido, este trabalho tem como objetivo investigar a aplicabilidade da técnica de IEM como ferramenta de monitoramento dos aspectos da integridade superficial e do desvio dimensional de amostras do aço SAE 52100 submetidas ao processo de retificação cilíndrica de mergulho com rebolo de óxido de alumínio branco. Os parâmetros de corte testados foram: tempo de centelhamento (0 e 5 s), velocidades de avanço (0,75 mm/min e 1,50 mm/min) e da peça (15 m/min e 30 m/min). Como variáveis de saída, foram mensurados os parâmetros de amplitude de rugosidade (Ra, Rq, Rvk, Rk e Rpk) e campo morfológico (Rsk, Rku), microdureza abaixo da superfície, desvios dimensionais do diâmetro, e as grandezas elétricas do processo. Os resultados mostraram que a baixa velocidade de avanço e centelhamento reduziram a rugosidade e desvios dimensionais. Por outro lado, o aumento de microdureza na peça a 30 μm abaixo da superfície foi influenciado pela alta velocidade da peça. Quanto à análise dos índices de danos a partir dos sinais de IEM das amostras, observou-se correlação forte do índice CCDM com a rugosidade Ra (90 a 95 kHz) e a microdureza (55 a 60 kHz), enquanto o desvio dimensional correlacionou-se tanto com o índice CCDM (25 a 30 kHz) quanto com RMSD5 na faixa de 60 a 65 kHz. |
| Abstract: | Among the peculiarities of grinding process with conventional abrasive grinding wheels high specific cutting energy highlights because it is responsible for most of heat generated to be transferred to workpiece, thereby potentializing the occurrence of thermal damages and distortions to the workpiece. For this reason, monitoring of workpiece surface integrity is crucial to ensure the quality of the finished product, especially using non-destructive methods. Among these methods, the electromechanical impedance (EMI), for example, poses as promising and reliable technique to monitor the integrity ground components. In this context, this work aims to investigate the applicability of the EMI technique as a tool for monitoring the surface integrity and dimensional deviation of SAE 52100 steel samples submitted to the plunge cylindrical grinding process with aluminum oxide grinding wheel. The cutting parameters were: sparkout time (0 and 5 s), feed rate (0.75 mm/min and 1.50 mm/min) and workspeed (15 m/min and 30 m/min). As output variables, amplitude roughness parameters (Ra, Rq, Rvk, Rk and Rpk) and morphological space (Rsk, Rku), microhardness below the machined surface, dimensional deviation, and the electrical measurements of the process. The results showed that at lower feed rate and sparkout time strongly affected on the reduction of surface roughness and dimensional deviation. On the other hand, the increase in the workpiece microhardness at about 30 μm below the machined surface was influenced primarily by the high workspeed. With respect to the analysis of the damage indexes from the EMI signals a strong correlation between the CCDM index and the roughness Ra (90 to 95 kHz) and microhardness (55 to 60 kHz) was noticed. For the dimensional deviation the correlation was observed either with the CCDM index (25 to 30 kHz) and by RMSD5 in the range of 60 to 65 kHz. |
| Palavras-chave: | Retificação cilíndrica Aço SAE 52100 Integridade superficial Desvio dimensional Impedância eletromecânica Cylindrical grinding SAE 52100 steel Surface integrity Dimensional deviation Electromechanical impedance |
| Área(s) do CNPq: | CNPQ::ENGENHARIAS::ENGENHARIA MECANICA |
| Assunto: | Engenharia mecânica Impedância (Eletricidade) Rebolos |
| Idioma: | por |
| País: | Brasil |
| Editora: | Universidade Federal de Uberlândia |
| Programa: | Programa de Pós-graduação em Engenharia Mecânica |
| Referência: | RESENDE, Paulo Vinicius da Silva. Análise da integridade da superfície e do desvio dimensional de aço rolamento pela técnica da impedância eletromecânica após retificação cilíndrica de mergulho. 2021. 114 f. Dissertação (Mestrado em Engenharia Mecânica) - Universidade Federal de Uberlândia, Uberlândia, 2021. DOI http://doi.org/10.14393/ufu.di.2021.5583 |
| Identificador do documento: | http://doi.org/10.14393/ufu.di.2021.5583 |
| URI: | https://repositorio.ufu.br/handle/123456789/32908 |
| Data de defesa: | 31-Ago-2021 |
| Aparece nas coleções: | DISSERTAÇÃO - Engenharia Mecânica |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| AnáliseDaintegridade.pdf | Dissertação | 6.26 MB | Adobe PDF |  Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.