Title: Análise das propriedades estruturais, morfológicas e mecânicas de duas marcas comerciais diferentes de dissilicato de lítio para o sistema CAD/CAM
metadata.dc.creator: Tavares, Lucas do Nascimento
metadata.dc.contributor.advisor1: Neves, Flávio Domingues das
metadata.dc.contributor.referee1: Zancopé, Karla
metadata.dc.contributor.referee2: Fernandes, Cláudio Pinheiro
metadata.dc.description.resumo: O objetivo deste presente estudo foi comparar duas marcas comerciais diferentes de Dissilicato de Lítio para o sistema CAD / CAM (IPS e.max CAD e Rosetta SM CAD / CAM), avaliando suas propriedades estruturais, morfológicas e mecânicas. Para avaliar as propriedades estruturais foram necessárias duas amostras de cada grupo, para serem analisadas por meio do DRX (difração de raios X). As propriedades morfológicas foram analisadas utilizando o MEV (Microscopia eletrônica de Varredura) antes e depois do tratamento térmico, e o teste de porosidade, realizado através de uma tomografia computadorizada em 3D (micro-CT). Para avaliar as propriedades mecânicas foi realizado o teste flexural de três pontos e o teste de microcisalhamento, e para isto foram selecionados dez espécimes de cada grupo para cada teste. Os valores médios de porosidade e da resistência flexural de três pontos foram analisados pelo teste t e a resistência de união obtida através do microcisalhamento foi analisada pelo teste Anova Two-way. Todos os testes usaram um nível de significância de α = 0,05. Os resultados obtidos pela análise estrutural realizada pelo DRX apresentaram picos no difractograma correspondentes ao Metassilicato de Lítio e o Dissilicato de Lítio, com intensidades semelhantes para ambos os grupos testados. Após realizar a microscopia eletrônica de varredura, não foi encontrado diferenças na morfologia dos cristais, em ambas as cerâmicas testadas, antes e depois do tratamento térmico. O teste de porosidade não mostrou diferença estatisticamente significativa entre o valor total de poros encontrados. Ambos os resultados dos testes mecânicos não apresentaram diferenças estatísticas significativas entre os grupos avaliados. Baseado nos resultados encontrados, não houve diferença entre as duas marcas comerciais testadas, em relação as suas propriedades estruturais, morfológicas e mecânicas.
Abstract: The aim of the present study was to compare two different brands of lithium disilicate CAD/CAM blocks (IPS e.max CAD and Rosetta SM CAD/CAM), evaluated by structural, morphological and mechanical properties. Two specimens of each group were analyzed using x-ray diffraction (XRD) to evaluate the structures of the ceramic material. Morphologic properties were analyzed using the Scanning Electron Microscopy (SEM) before and after the heat treatment; and porosity test was performed using a 3D micro-computed tomography analyses (micro-CT). Ten specimens of each group were submitted to three-point flexure strength and microshear bond strength tests, to analyze the mechanical properties of both brands. Mean values of porosity test and three-axial flexural strength were analyzed by t Test, and the microshear bond strength was analyzed by Anova two-way. All tests used a significance level of α=0.05. The structure results performed by XDR, presented high peak positions corresponding to the standard lithium metasilicate and lithium disilicate, with similar intensities for both tested groups. The morphologic results demonstrated similar patterns of crystalline structure, before and after the heat treatment and the porosity test showed no difference between the number and size of the pores found. Both mechanical tests results did not present statistically significant differences between the samples. Based on the results, there was no difference in relation to their structural, morphological and mechanical properties, between the two commercial brands tested.
Keywords: Odontologia
Litio
Microscopia eletrônica de varredura
Sistema CAD/CAM
Dissilicato de lítio
DRX
MEV
Microcisalhamento
Resistência de união
Resistência flexural
Lithium disilicate
SEM
Microshear bond strength
Flexural strength
CAD/CAM system
metadata.dc.subject.cnpq: CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal de Uberlândia
metadata.dc.publisher.program: Programa de Pós-graduação em Odontologia
Citation: TAVARES, Lucas do Nascimento. Análise das propriedades estruturais, morfológicas e mecânicas de duas marcas comerciais diferentes de dissilicato de lítio para o sistema CAD/CAM. 2017. 55 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Uberlândia, Uberlândia, 2017.
URI: https://repositorio.ufu.br/handle/123456789/18174
Issue Date: 14-Feb-2017
Appears in Collections:DISSERTAÇÃO - Odontologia

Files in This Item:
File Description SizeFormat 
AnalisePropriedadesEstruturais.pdfDissertação3.78 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.