Title: Influência do nióbio na textura e resistência à corrosão de aços inoxidáveis ferríticos em ambientes aerados e desaerados
Other Titles: Influence of niobium on the texture and corrosion resistance of ferritic stainless steels in aerated and de-aerated environments
metadata.dc.creator: Ardila, Miguel Angel Narvaez
metadata.dc.contributor.advisor1: Mello, José Daniel Biasoli de
metadata.dc.contributor.referee1: Silva Junior, Washington Martins da
metadata.dc.contributor.referee2: Canobre, Sheila Cristina
metadata.dc.contributor.referee3: Probst, Sonia Maria Hickel
metadata.dc.description.resumo: O objetivo deste trabalho é estudar a influência do nióbio na textura cristalográfica e resistência à corrosão de aços inoxidáveis ferríticos em ambientes aerados e desaerados. Usou-se para o estudo os aços inoxidáveis ferríticos P409, P410, P430A, P430E (estabilizado ao Nb) e como objetos de comparação usaram-se os aços inoxidáveis austenítico P304 e o aço ao carbono A36. Neles realizou-se uma caracterização mecânica (dureza, ensaio de tração), e para os aços P430A e P430E foi feita uma caracterização cristalográfica (via EBSD) por meio de figura de polos inversa (IPF) e da função de distribuição de orientação cristalina (FDOC). As amostras foram submetidas a ensaios de polarização potenciodinâmica anódica para soluções de 3,56% NaCl e 1N de H2SO4 em ambiente aerado e solução de 3,56% NaCl em ambiente desaerado. As amostras foram examinadas por microscopia MEV após os ensaios de polarização. A análise dos resultados mostrou claramente que a textura cristalográfica influência a resistência à corrosão. O nióbio diminui a presença de orientações preferenciais, e, por consequência, a influência da textura na resistência à corrosão, no entanto aumenta a resistência à corrosão nos aços inoxidáveis pela formação de carbonetos de nióbio. Por último observou-se que para ensaios de polarização em ambientes aerados e desaerados existe uma ligeira variação no comportamento que depende de cada aço, mas que não é estatisticamente significativa.
Abstract: This work aims to study the niobium influence in the crystallographic texture and the corrosion resistance of ferritic stainless steels on aerated and de-aerated environments. For this objective the ferritic stainless steels P409, P410, P430A, P430E (Nb stabilized) were used; and austenitic stainless steel, P304, and carbon steel, A36, were used as comparative materials. These materials had a mechanical characterization (hardness and tension test), and the steels P430A and P430E had a crystallographic characterization too. That crystallographic characterization (by EBSD) was analyzed through to inverse pole figure (IPF) and crystal orientation distribution function (CODF). The samples were submitted to anodic potentiodynamic polarization test in solutions: 3.56% NaCl, and 1N H2SO4 on aerated environment, and 3.56% NaCl at de-aerated environment. The samples were examined by SEM after the polarization tests. The analysis of the results clearly showed that the crystallographic texture influence the corrosion resistance. The niobium in the stainless steel reduces the presence of preferential orientation, therefore, the influence of the texture in the corrosion resistance, but helps to increase the corrosion resistance by the formation of niobium carbbonites. Finally it was observed that for polarization tests in aerated environments and de-aerated have a very small variation in behavior that depends on the steel, but this variation is not statistically significant.
Keywords: Polarização potenciodinâmica
Corrosão
Textura cristalográfica
Elementos estabilizadores
Ambiente aerado
Ambiente desaerado
Aços inoxidáveis
Potentiodynamic polarization
Corrosion
Crystallographic texture
Stabilizing elements
Aerated environment
De-aerated environment
Stainless steels
Corrosão e anticorrosivos
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
metadata.dc.language: por
metadata.dc.publisher.country: BR
Publisher: Universidade Federal de Uberlândia
metadata.dc.publisher.initials: UFU
metadata.dc.publisher.department: Engenharias
metadata.dc.publisher.program: Programa de Pós-graduação em Engenharia Mecânica
Citation: ARDILA, Miguel Angel Narvaez. Influence of niobium on the texture and corrosion resistance of ferritic stainless steels in aerated and de-aerated environments. 2013. 108 f. Dissertação (Mestrado em Engenharias) - Universidade Federal de Uberlândia, Uberlândia, 2013.
URI: https://repositorio.ufu.br/handle/123456789/14935
Issue Date: 26-Feb-2013
Appears in Collections:DISSERTAÇÃO - Engenharia Mecânica



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.