Title: Influência de modificações superficiais (cromagem e texturização) no comportamento tribológico de aços para fabricação de cilindros de laminação a frio
Other Titles: Influence of surface modifications (surface texturing and hard chromium coating) on the tribological behavior of cold rolling mills Rolls steels
metadata.dc.creator: Gonçalves Júnior, José Lúcio
metadata.dc.contributor.advisor1: Mello, José Daniel Biasoli de
metadata.dc.contributor.referee1: Costa, Henara Lillian
metadata.dc.contributor.referee2: Silva, Carlos Henrique da
metadata.dc.contributor.referee3: Serantoni, Claudia Regina
metadata.dc.description.resumo: O presente trabalho analisou o comportamento tribológico de modificações, geralmente utilizado em cilindros para laminação a frio. Iniciou‐se o processo com a produção das amostras a partir de um fragmento de cilindro de laminação que foi cortado, originando amostras de aproximadamente 30 x 30 mm, em que se fez tratamento térmico, retificação de ambas as faces e modificações superficiais de cromagem, texturização, cromagem com posterior texturização e texturização com posterior cromagem. Os testes de desgaste foram realizados em modo alternado de deslizamento, com configuração de esfera sobre um plano utilizando‐se carga de 9,8 N. Os resultados permitiram concluir que a texturização elevou os parâmetros topográficos, enquanto o revestimento de cromo duro diminuiu os mesmos. Observou‐se que não houve alteração significativa do coeficiente de atrito em função das modificações superficiais e que a texturização promoveu um aumento significativo no desgaste do contracorpo, enquanto o revestimento de cromo duro promoveu uma redução do mesmo. A adição do revestimento de cromo duro promoveu a formação de uma tribocamada no contracorpo constituída de cromo e oxigênio, em contrapartida, em corpos sem o recobrimento de cromo duro ocorreu a formação de uma tribocamada constituída de ferro e oxigênio nas amostras. Em função da combinação da baixa carga aplicada e do curto intervalo de tempo, tornou‐se impossível a quantificação do desgaste nos corpos pelas diferentes técnicas empregadas. Adicionalmente, estudaram‐se sete diferentes materiais utilizados em réplicas, sendo executadas análises quantitativas e qualitativas via interferometria a laser e microscopia eletrônica de varredura. Dos materiais analisados, o material Facsimile apresentou melhores qualidades de replicação.
Abstract: The present work analyzed the tribological behavior of surface modifications often used in cold rolling mill rolls. Different surface modifications were carried out on samples produced from a fragment of the rolling mill roll: i) texturing; ii) chromium plating; iii) texturing with subsequent hard chrome plating; iv) and hard chrome plating with subsequent texturing. The roll samples were subsequently heat treated and ground on both faces resulting in dimensions of approximately 30 x 30 mm. The wear tests were performed using a reciprocating movement of a ball over flat configuration under a load of 9.8 N. The results showed that surface texturing increased the topographic parameters whereas hard chrome coating decreased them. It was observed that there was no significant change in the coefficient of friction as a function of surface modification. Surface texturing increased the wear of the counter body, while the hard chromium coating reduced it. The addition of the hard chromium coating promoted the formation of a tribolayer on the counter body consisting of chromium and oxygen. On the other hand, for the samples without hard chrome coating the tribolayer consisted of iron and oxygen. As a consequence of the low applied load and the short duration of the tests it became impossible to quantify the wear on the bodies using various techniques. Additionally seven different materials used in replicates. Were investigated using quantitative and qualitative analysis via laser interferometry and scanning electron microscopy. Amongst materials tested, the material Facsimile presented best capacity of replication.
Keywords: Laminação a frio
Revestimento de cromo duro
Texturização
Triboloy
Cold mill
Hard chrome plating
Texturing
Tribologia
Laminação (Metalurgia)
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
metadata.dc.language: por
metadata.dc.publisher.country: BR
Publisher: Universidade Federal de Uberlândia
metadata.dc.publisher.initials: UFU
metadata.dc.publisher.department: Engenharias
metadata.dc.publisher.program: Programa de Pós-graduação em Engenharia Mecânica
Citation: GONÇALVES JÚNIOR, José Lúcio. Influence of surface modifications (surface texturing and hard chromium coating) on the tribological behavior of cold rolling mills Rolls steels. 2011. 93 f. Dissertação (Mestrado em Engenharias) - Universidade Federal de Uberlândia, Uberlândia, 2011.
URI: https://repositorio.ufu.br/handle/123456789/14899
Issue Date: 7-Oct-2011
Appears in Collections:DISSERTAÇÃO - Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
d.pdf7.63 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.